Graphite/epoxy (T300/5208) and graphite/polyimide composites (C6000/PMR 15) were exposed to various levels of 0.5 MeV electron radiation with the maximum dose being 10,000 Mrad. A three point bending test was used to evaluate the ultimate stress and modulus of the composites. In all composites except transverse samples of C6000/PMR 15 ultimate stress values remained approximately constant or increased slightly. The modulus values remained approximately constant for all composite types regardless of the radiation level. Interfacial aspects of composites were studied. Interlaminar shear tests were performed on T300/5208 and C6000/PMR 15 composites irradiated to 10,000 Mrad. There was an initial increase in interlaminar shear strength (up to 1,000 Mrad) followed by a sharp decrease with further radiation exposure. Using scanning electron microscopy no visual differences in the mode of fracture could be detected between ruptured control samples and those exposed to various levels of radiation. Electron spectroscopy for chemical analysis (ESCA) revealed little change in the surface elements present in control and highly irradiated T300/5208 composite samples.